Effect of hydrolysis degree of hydrolyzed polyacrylamide grafted carboxymethyl cellulose on dye removal efficiency

In this present work, a series of hydrolyzed polyacrylamide grafted carboxymethyl cellulose (CMC-g-HPAM) was prepared. The structure and solution properties of CMC-g-HPAM were characterized by FTIR, ¹H-NMR, elemental analysis and zeta potential measurements. The graft copolymers were applied as flocculants to remove methylene blue (MB), a cationic dye, from aqueous solutions. In comparison with its precursors, carboxymethyl cellulose (CMC) and polyacrylamide CMC-g-PAM, CMC-g-HPAM exhibited higher removal efficiencies. Furthermore, the flocculation performance of the copolymers was significantly improved with the increase of the hydrolysis degree, and the MB removal efficiency was more than 90 % when the hydrolysis degree of CMC-g-HPAM was higher than 80 %. More importantly, image analysis in combination with fractal theory demonstrated that the graft copolymers could produce notably denser and larger flocs, which was of great significance in practical water treatment. The improved flocculation performance was ascribed to both charge neutralization and bridging effects.     

Preparation and characterization of oxidized regenerated cellulose film for hemostasis and the effect of blood on its surface

Hemostatic effects of oxidized regenerated cellulose (ORC) are well-known but its mechanism has never been demonstrated clearly. Since thrombus formation is a kind of surface phenomenon, we changed the morphology of cellulose to form a kind of membrane with ionic liquid as solution, and also we prepared ORC films with nitrogen dioxide(NO₂)/carbon tetrachloride(CCl₄) oxidation system reacting for 16, 40, 64 and 88 h, respectively. FTIR and NMR spectra showed that NO₂/CCl₄ oxidation system had a high selectivity on hydroxyl group at C6 of regenerated cellulose. With the oxidation time prolonging, the carboxyl content was enhanced and the DP was reduced. The XPS results suggested that a new carboxyl bond was formed due to the increasing of oxygen content. From contact angle analysis, the wettability of blood on the ORC film surface was better than that of the regenerated cellulose film, which was beneficial for the blood to spread. SEM photographs showed that the ORC film oxidized for 40 h could adsorb and activate more platelets and erythrocytes. Hemostatic evaluation and enzyme-linked immunosorbent assay indicated that the ORC film had a dramatic hemostatic performance, and the products of platelets release reaction, activated platelets glycoprotein and activated clotting enzymes were increased simultaneously. Moreover, the possible mechanism of the hemostasis for ORC film was discussed.     

UPLC-MS/MS法同时测定土壤中3种磺酰脲类除草剂残留

建立了QuEChERS法–超高效液相色谱–串联质谱法(UPLC-MS/MS)快速测定土壤中噻吩磺隆、苯磺隆、氯嘧磺隆3种磺酰脲类除草剂的方法。采用振荡提取、QuEChERS法净化方法处理土壤样品,利用UPLC-MS/MS分析,在多反应监测(MRM)模式下以0.1%甲酸水和乙腈为流动相梯度洗脱。3种除草剂在0.5~500μg/L的质量浓度范围内线性关系良好,相关系数为:0.996~0.999。在10,50μg/kg水平下进行加标回收实验,平均回收率为81.4%~92.9%,RSD为5.5%~10.6%,方法检出限(S/N=3)为0.12~0.16μg/kg。方法可用于大量实际土壤样品中3种除草剂的检测。     

Li+掺杂对Y2SiO5:Pr3+上转换发光性能影响

采用溶胶-凝胶法制备Li+掺杂改性的Y2SiO5:Pr3+上转换发光材料,考察了Li+掺杂对样品晶型及发光性能的影响。采用XRD,DSC-TGA,FS对所制备的材料进行表征,结果表明Li+掺入浓度在7%～8%(摩尔分数)之间会引起Y2SiO5晶体类型由X1型转变为X2型,且Li+掺入后样品转晶型温度由950℃降至800℃;样品经800℃煅烧处理后以X1型Y2SiO5为主相,850℃煅烧处理后以X2型Y2SiO5为主相;Li+掺入同时会提高Y2SiO5:Pr3+材料的上转换发光强度,Li+最佳掺杂浓度为10%,对于双掺杂Pr3+,Li+:Y2SiO5体系中Pr3+最佳掺杂浓度为1.2%。     

Eu（TTA）3AA-NBR/PVP同轴超细纤维的制备及荧光性能研究

用同轴静电纺丝制备了含有稀土铕配合物(Eu(TTA)3AA)的芯-壳结构的丁腈橡胶/聚乙烯吡咯烷酮(NBR/PVP)超细荧光纤维。考察了在外层PVP纺丝参数不变的情况下,改变芯层丁腈橡胶纺丝液的纺丝速度、Eu(TTA)3AA含量等对纤维形貌的影响。通过研究Eu(TTA)3AA-NBR/PVP同轴超细纤维中Eu(TTA)3AA微观结构、含量与纤维的荧光性能之间的关系,发现在同轴纤维形成过程中由于溶剂的快速挥发可使Eu(TTA)3AA形成无定形结构,进而在纤维中形成分子簇级别的分散,在Eu(TTA)3AA含量为30%时,同轴纤维比Eu(TTA)3AA粉末的荧光强度提高了2倍。     

稀土元素在含残余砷、锡09Cr2AlMoRE钢中的作用

对加稀土前后09Cr2AlMoRE钢取样分析化学成分,制备金相样用SEM-EDS研究了钢中析出物特征,制备透射电镜(TEM)试样通过TEM研究元素的晶界偏聚,并用热力学计算了稀土Ce,La,S和残余元素As反应固定残余元素As的可能性。研究结果表明:在低氧、硫的条件下,稀土镧可以和09Cr2AlMoRE钢中较低含量的砷(130×10-6)作用生成镧砷金属间化合物;铈、镧主要是通过形成稀土砷硫夹杂物固定钢中残余元素砷。另外,在本实验条件下稀土元素(64×10-6)只有很微量的偏聚在晶界,残余元素As不在晶界偏聚。     

含芳酰胺结构的新型甲壳型液晶高分子PMPACS的聚合反应动力学研究

采用称量法和GPC,研究了以二甲基乙酰胺为溶剂,偶氮二异丁腈为引发剂,自由基溶液聚合制备含芳酰胺结构的新型甲壳型液晶高分子聚[乙烯基对苯二甲酸二(4-甲氧基苯胺)](PMPACS)的聚合反应动力学.研究发现,(1)MPACS的聚合反应在60℃时主要为双基偶合终止,所以反应后期聚合物分子量明显增大,分子量分布变窄;(2)该反应的聚合反应速率方程为Rp=kp[M][I]1/2,表观活化能Eα=44 kJ/mol,在60℃时的聚合反应常数kp=1.04 L·mol-1·h-1;(3)相同聚合条件下,单体的转化率和数均分子量随单体初始浓度[M]0的增加而增大,当引发剂浓度[I]0增加时,聚合物的分子量随之降低,分子量分布增大;(4)该研究虽采用普通自由基聚合,所得聚合物的分子量分布却较窄,仅为1.1～1.4.     

用于直接甲醇燃料电池的侧链型磺化聚芳醚酮/聚乙烯醇交联膜的制备与性能研究

以高磺化度的侧链型磺化聚芳醚酮(S-SPAEK)和聚乙烯醇(PVA)为原料,通过溶液共混的方法在120℃下制备了PVA含量不同的S-SPAEK/PVA交联膜.红外光谱图表明S-SPAEK聚合物中的磺酸基团与PVA中的羟基反应生成酯键而形成共价交联.通过对交联膜的性能测试发现PVA的引入明显降低了膜的甲醇渗透系数,改善了膜的溶胀性,提高了膜的保水能力.S-SPAEK/PVA(85/15)交联膜水的脱附系数从S-SPAEK的3.1×10-8 cm2/s降低到2.9×10-9 cm2/s.在25℃和60℃时S-SPAEK/PVA(85/15)交联膜的甲醇渗透系数分别为2.6×10-7cm2/s和3.9×10-7cm2/s,明显低于相同温度下的纯S-SPAEK膜的8.1×10-7cm2/s与14.5×10-7cm2/s,而其质子传导率虽然有所下降,但是在25℃和80℃时分别达到了0.055 S/cm和0.083 S/cm,能够满足直接甲醇燃料电池(DMFCs)对质子交换膜的要求,有望在DMFCs中得到应用.     

酸性条件下硅醇盐Si(OCH_3)_4水解与聚合机理的密度泛函研究

用密度泛函方法在B3LYP/6-31G(d,p)基组水平上对反应系统中的所有物种进行全优化,用CPCM溶剂模型在同一基组水平上进行了单点计算,系统研究了硅醇盐前驱体Si(OCH3)4在酸性条件下的水解、聚合机理,阐明了二者的相互竞争关系.研究发现,H2O以氢键或配位键与前驱体结合,然后通过氢转移完成水解;水分子从质子化烷氧基的对面键合并发生水解;第4级水解是H2O从对位驱逐质子化烷氧基,但不能水解完全;水解产物通过"环状模式",由氢键结合成多元环,然后发生氢转移并完成聚合;水解过程的能垒明显低于聚合过程;H+阻止水解产物聚合成环;硅正离子可引发无垒聚合反应,但在能量上并不可行.     

用加速溶剂萃取及制备型高效液相色谱法从烟梗中制取多酚对照品

提出用加速溶剂萃取及制备型高效液相色谱方法从烟梗中提取、制备多酚对照品的方法。样品粉碎后以乙醇(80+20)溶液为萃取溶剂经加速溶剂萃取仪在110℃静态萃取10min,提取液氮气吹扫60s后过MCI树脂和Sephadex LH 20凝胶净化,流出液用丙酮定容后,先通过制备型高效液相色谱初步分离,再通过半制备高效液相色谱进一步分离,得到5个多酚类化合物,经核磁共振波谱法鉴定分别为芸香苷、绿原酸、槲皮素、柚皮素和咖啡酸甲酯。5个多酚类化合物的纯度均大于99%,故可用作多酚对照品。